1005
Taile
| 包装: | |
|---|---|
| Availability: | |
| Quantity: | |
Taile 1005 is a 10:1 two-component modified acrylic structural adhesive, white after mixing. It features outstanding adhesion to PP, PE and other low surface energy hard-to-bond plastics without primer. Tack-free in 6~8 minutes at 25℃, shear strength ≥5MPa. Great flexibility, low internal stress, ideal for assembly of PP, PE, plastic-metal composite parts.
Core Advantages
Bond PP, PE without surface primer: Solve bonding difficulty of low surface energy polyolefin plastics
Good flexibility after curing, low internal stress, prevent assembly parts cracking
Medium open time, tack-free within 6~8 minutes @25℃, convenient for workpiece alignment
High bonding strength, overlap shear strength ≥25MPa after full curing
Good adhesion to ABS, PC, aluminum alloy and most common engineering plastics
Parameter | Taile 1005 | Taile 1167 | Taile 1585 |
Mixing Ratio | 10:1 | 10:1 | 10:1 |
Mixed Color | White | Light Blue | Light Blue |
Tack-Free Time @25℃ | 6~8 min | 7~8 min | 5~6 min |
Shear Strength | ≥5MPa | ≥20MPa | ≥20MPa |
Typical Use | PP/PE plastic parts assembly | PC/ABS & aluminum alloy housing | Electronics assembly with strict odor requirements |
Odor Level | Standard | Standard | Low Odor |
Key Feature | Bond PP, PE hard-to-bond plastics | Long open time for general electronic housings | Low odor, ideal for workshop use |
Basic Technical Data
Mix Ratio(A:B): 10 : 1 by volume
Mixed Color: White
Tack-Free Time: 6~8 min (25℃)
Overlap Shear Strength: ≥5 MPa
Appearance: Thixotropic paste, non-sagging
Typical Applications
Assembly bonding for PP, PE plastic shells, plastic-metal composite components, household appliances accessories, consumer electronic plastic parts and general industrial hardware.