Two-component polyurethane system, mix ratio A:B = 1:5 by weight
UL-94 V0 flame retardant grade
Complies with RoHS and REACH environmental requirements
Excellent adhesion after curing
Good physical and electrical properties
Waterproof, sealing, filling, and insulation protection
Effectively ensures stability and reliability of components
Operating temperature: -40~130℃
Hardness: Shore-D 66±5D
Thermal conductivity: 0.6±0.05 W/m·K
Dielectric strength: >24 kV/mm
Volume resistivity: ≥1×10^14 Ω·cm
Water absorption (24-48h, 25℃): ≤0.5%
Flame Retardant Grade | UL-94 V0 |
Application | Capacitors, transformers, sensors, controllers, wire harnesses, charging pile controllers, automotive electronics |
Feature | Flame retardant, waterproof, sealing, filling, insulation, good adhesion |
Packaging | Multiple sizes available |
Shelf Life | 6 months |
Capacitors
Small transformers
Transformers (instrument transformers)
Sensors
Controllers
Wire harnesses
Charging pile controllers
Automotive electronics
Electronic component potting and protection
Stir Component A before use to avoid sedimentation and irregular metering.
Mix Component A and B at the specified ratio (A:B = 1:5 by weight) thoroughly.
For surfaces requiring a smooth, bubble-free finish or components with many small gaps, vacuum defoaming or vacuum dispensing is recommended after mixing A and B.
Ensure bonding surfaces are dry, free of oil, dust, or other contaminants.
For accelerated curing, place the dispensed parts in a temperature-controlled oven or tunnel furnace after dispensing, and control the temperature within the process requirements.
Liquid Parameters (25℃):
Item | Component A | Component B | A+B Mixed |
|---|---|---|---|
Appearance | Brown | Black / Light Yellow / White | — |
Viscosity (mPa·s) | 30±10 | 11000±4000 | 1100±500 |
Density (g/cm³) | 1.20±0.05 | 1.51±0.05 | 1.49±0.05 |
Pot Life (100g, 25℃) | — | — | 39±5 min |
Tack-Free Time (100g, 25℃) | — | — | 6-7 H |
Curing (100g) | — | — | 25℃ basic curing 7-8H |
Cured Properties:
Item | Result |
|---|---|
Color | Black / Beige / White |
Hardness | Shore-D 66±5D |
Operating Temperature | -40~130℃ |
Water Absorption (24-48h, 25℃) | ≤0.5% |
Thermal Conductivity | 0.6±0.05 W/m·K |
Dielectric Strength (25℃) | >24 kV/mm |
Volume Resistivity (25℃) | ≥1×10^14 Ω·cm |
Flame Retardant Grade | UL-94 V0 |
(Same as Section 8, retained as requested)
Stir Component A before use to avoid sedimentation and irregular metering.
Mix Component A and B at the specified ratio (A:B = 1:5 by weight) thoroughly.
For surfaces requiring a smooth, bubble-free finish or components with many small gaps, vacuum defoaming or vacuum dispensing is recommended after mixing A and B.
Ensure bonding surfaces are dry, free of oil, dust, or other contaminants.
For accelerated curing, place the dispensed parts in a temperature-controlled oven or tunnel furnace after dispensing, and control the temperature within the process requirements.
Packaging:
Multiple packaging sizes are available. Please contact your sales engineer for packaging sizes and availability.
Storage & Transportation:
This product is non-dangerous goods and can be stored and transported as general chemicals.
Store in a ventilated, dry warehouse at 20~30℃, away from direct sunlight. Shelf life is 6 months.
After opening, please use as soon as possible. If not used up, tighten the cap and use within 3 days for best results. If the opened adhesive cannot be used up within 7 days, test for abnormalities before subsequent use.
When the adhesive is placed in the tank, vacuum preservation should be applied during downtime. A moisture filter device should be installed on the air inlet valve to ensure the adhesive does not contact moisture. Do not store for more than 7 days.
RoHS
REACH
UL-94 V0